污泥和石英砂尾矿制备建材陶粒的烧结时间研究
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

X705

基金项目:

2013年地方高校国家级大学生创新创业训练计划项目(201311535004)


Study of the sintering time on the effects of ceramsite made from sewage and quartz tailing
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以城市污水处理厂的污泥与石英尾砂为主要原料,添加适当助剂如河道底泥、矿山浮选脱硫废渣,可制备建材陶粒.在原料配比 m(石英尾砂)∶m(污泥)∶m(粘合剂)∶m(河道底泥)=4∶4∶3∶3、进料温度400℃、预热时间20 min、焙烧温度1100℃、焙烧时间25 min 的条件下,制备的陶粒强度为5.11 MPa,吸水率为11.7,,堆积密度为913 kg/m3.

    Abstract:

    Based on the municipal sewage sludge and quartz tailing,added appropriate additives such as river sediment and mine flotation desulfurization sludge,the lightweight ceramsite could be prepared for the build materials.The ratio of raw material is m (quartz tailing)∶m (sewage)∶m (adhesive)∶m (river sediment)=4∶4∶3∶3,and feed temperature is 400℃ and preheating time is 20 min and heating time is 25 min and sintering temperature is 1 100℃,respectively.The strength of ceramsite is 5.1 1 MPa,and the water absorption rate is 1 1.7,,and the density is 913 kg/m3 .

    参考文献
    相似文献
    引证文献
引用本文

郭夙琛,阮德明,邹辉煌,王强,闫淑,贺玲玲,王湘英.污泥和石英砂尾矿制备建材陶粒的烧结时间研究[J].材料研究与应用,2015,(2).

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2020-04-26
  • 出版日期:
文章二维码
材料研究与应用 ® 2024 版权所有