Abstract:The purpose of this work was research into influence of ultra-violet radiation on size of run of regional and screw dislocations in beams of dislocation sockets, formed at indentation surface of alkali-halide crystals. In experiments it was used crystals NaCl, with the quantitative maintenance of impurity 10-2 -10-3weight，, the wave length of UV-radiation λ=250 nanometers, the sizes of samples 10mm× 20mm× 2mm,temperature of samples was constant T=290 K.It is established that indentation and the simultaneous irradiation of samples a ultraviolet is increases size of run of head dispositions in dislocation sockets..It is marked, that influence UV-radiation nonequivalence for various times of an exposition. At small times (till 5 minutes) the size of run grows. The length of beams increases on ～ 50 ，. At the further increase in time of influence of a ultraviolet the length of beams is reduced till the sizes corresponding stressing without an irradiation (Figs. 1, 2, 3). The effect is observed on dislocation beams of regional and screw orientations and most expressed at small loadings (in our experiments-10 grams) (Fig. 3).Observable effects are explained from positions dislocation-exciton interactions. At UV-radiation exciton cooperates with the charged step on a disposition, causing movement of a step along a disposition on one internuclear distance. Due to this interaction overcoming by a disposition of a grid of stoppers is facilitated.Big times of endurance cause a relaxation of pressure directly in a print that provides convertible movement of dispositions in area of a print and as consequence, reduction of length of beams of dislocation sockets.